PVC(polyvinyl chloride) Sheet was treated in 0~7 M NaOH solutions at 150~250oC for 0~12 hr, in order to study the behavior of degradation and characteristics of residues in waste plastics. The degree of weight loss due to the decomposition reached 31% for the reaction in 3 M NaOH over 225oC for oh, which corresponded to the loss of all the plasticizer contained in PVC Sheet. Under the same conditions, DOP was hydrolyzed quantitatively to phthalic acid and isooctyl alcohol by the alkali catalyst. In the hydrothermal reaction, the pores in size 5~10 mm were produced in the sheet by the hydrolysis of DOP, besides dehydrochlorination of PVC produced smaller pores. The pore size became smaller, about 1~8 mm for 12 h, along with time.
연질 PVC(polyvinyl chloride)sheet를 0~7 M NaOH 수용액 중에서 반응온도 150~250oC, 반응시간 0~12시간으로 처리하여 폐플라스틱의 분해거동 및 잔류물의 특성에 관해서 검토하였다. 225oC, 3 M NaOH, 0시간에 있어서 PVC sheet의 중량감소율은 약 31%에 도달하였으며, 이 값은 PVC sheet에 포함된 가소제의 손실과 거의 비슷하였다. 똑같은 조건하에서 DOP는 알카리 촉매에 의해 프탈산과 이소옥탄올로 정량적으로 가수분해되었다. 이 수열작용에서 DOP의 가수분해로 인해 5~10 mm 세공이 관찰되어졌고, 탈염화수소의 촉진과 더불어 세공이 더욱 작아져 반응시간이 길면 길수록 세공의 크기가 12시간에서는 약 2 mm 정도가 되었다.
Click the PDF button.
- Publisher :The Korean Society of Mineral and Energy Resources Engineers
- Publisher(Ko) :한국자원공학회
- Journal Title :Journal of the Korean institute of mineral and energy resources engineers
- Journal Title(Ko) :한국자원공학회지
- Volume : 39
- No :4
- Pages :242-247
Journal of the Korean Society of Mineral and Energy Resources Engineers