Kaolinite was treated with titanate coupling agents and then used for contact angle measurement after compaction. The results show that the contact angle increases with increasing concentration of titanate coupling agents. For the case of kaolinite treated with Isopropyl triisostearoyl titanate(KR TTS), the maximum contact angle was observed at 105o, which was close to that of the monolayer of pure stearic acid. The modified kaolinite samples were studied by inverse gas chromatography. The dispersive component of the solid surface free energy( gSD) was determined for these samples. The gSD values were generally less the modified samples. For the KR TTS, the gSD of the modified kaolinite at 150oC exhibits surface energy close to that(28.3 mJ/m2) of polyethylene, with no surface polarity. The values of gSDof all the samples decrease with increasing temperature.
티타네이트 커플링제로 표면개질한 카올리나이트를 평탄한 판으로 압축했다. 접촉각 측정법에 의해서 측정한 접촉각은 티타네이트 커플링제의 농도가 증가함에 따라 증가한다. Isopropyl triisostearoyl titanate(KR TTS)에 대해서, 표면개질한 카올리나이트의 최대 접촉각은 순수한 스테아린산 단분자층의 접촉각과 거의 같은 값(105o)을 갖는다. 표면 개질한 카올리나이트의 시료들은 IGC에 의해서 분산 표면자유에너지( gSD)가 측정되었다. gSD는 전반적으로 표면 개질한 시료에서 더 작았다. KR TTS에 대해서, 표면개질한 카올리나이트의 gSD 는 150oC에서 표면이 무극성인 폴리에틸렌의 값(28.3 mJ/m2)과 거의 같은 값을 보이고 있다. 모든 시료의 gSD 값은 온도가 증가함에 따라 감소한다.
Click the PDF button.
- Publisher :The Korean Society of Mineral and Energy Resources Engineers
- Publisher(Ko) :한국자원공학회
- Journal Title :Journal of the Korean institute of mineral and energy resources engineers
- Journal Title(Ko) :한국자원공학회지
- Volume : 38
- No :1
- Pages :27-34
Journal of the Korean Society of Mineral and Energy Resources Engineers