Dry beneficiation was applied to remove impurities from Daemyoung WB-grade kaolin. To obtain the optimum condition, disintegration test for the liberation of impurity and separation test for removal of impurity from kaolin as well as the characteristics of the raw ore were investigated. The result showed that 71.4% yield was obtained and its composition was SiO2 44.3%, Al2O3 37.0%, Fe2O3 0.99%, CaO 1.2%, TiO2 0.12% when the sample was disintegrated using an impact mill. Taking into account of the yield, the sample less than 43 mm was recovered by air classifier. As a result of that 70.1% recovery was obtained and its composition was SiO2 44.6%, Al2O3 37.4%, Fe2O3 0.96%, CaO 1.2%, TiO2 0.12%. The plasticity and calcined whiteness were increased to 33.0% and 95.35, respectively. This result indicates that the purified Daemyoung WB-grade kaolin can be used as a raw materials for high-grade ceramics.
대명 고령토에 혼입된 불순물을 제거하기 위하여 건식 정제를 행하였다. 동 정제의 최적조건을 얻기 위하여 원료광물의 물리 화학적 특성분석, 단체분리를 위한 해쇄실험, 불순물과 고령토의 분리를 위한 건식 분급 실험을 수행하였다. 충격식 분쇄기를 사용한 해쇄실험결과 -325 mesh 산물을 71.4%로 생산할 수 있었으며, 그 산물의 품위는 SiO2 44.3%, Al2O3 37.0%, Fe2O3 0.99%, CaO 1.2%, TiO2 0.12% 이었다. 생산율을 고려하여 43 mm 이하의 입자를 건식분급에 의하여 회수하면 정제 고령토의 생산율은 70.1 wt.% 이었으며, 그 산물의 품위는 SiO2 44.6%, Al2O3 37.4%, Fe2O3 0.96%, CaO 1.2%, TiO2 0.12% 이었다. 정제 고령토의 가소성과 소성 백색도는 33.0% 및 95.35로 각각 향상되었다. 이 결과로부터 정제된 대명 WB 급 고령토는 고급 도자기 원료로 사용할 수 있다는 것을 알 수 있었다.
Click the PDF button.
- Publisher :The Korean Society of Mineral and Energy Resources Engineers
- Publisher(Ko) :한국자원공학회
- Journal Title :Journal of the Korean institute of mineral and energy resources engineers
- Journal Title(Ko) :한국자원공학회지
- Volume : 37
- No :3
- Pages :159-165
Journal of the Korean Society of Mineral and Energy Resources Engineers