PVC를 염소원으로 하는 염화배소에 의한 전기로 제강분진으로부터 유가금속의 회수: 이계승, 송영준

31 December 2003. pp. 446-456

PDF

Abstract

To investigate the possibility of using waste plastic in recycling of E.A.F.(Electric Arc Furnace) dust, pure PVC(polyvinyl chloride) powder were mixed with E.A.F.dust and made as pellets and roasted. Under rapid heating at 1000℃, 66% of HCl delivered from PVC was reacted with the dust and 20% Fe was volatilized. Under slow heating rate of 2℃/min, however, 95.3% HCl was reacted with the dust and Fe was not volatilized. In this slow condition, FeCl2 reacted with franklinite and formed ZnCl2 and Fe3O4 in 600℃ or higher temperature. From the pellet containing 40% PVC, 96.2% Zn, 97.4% Pb and 98.8% Cd of the dust were recovered by heating the pellet in 2℃/min to 800℃. The residue after recover the metals contains 46% Fe and 20.9% C, and can be used in steel making process.

Keywords

E.A.F. Dust

Recycling

PVC

Roasting

Volatilized

Recovered

전기로 제강공정에서 발생되는 분진의 재활용에 PVC를 활용하고자 국내 I社의 전기로 분진과 PVC분말을 혼합하여 제조한 펠릿을 소정의 조건에서 가열하면서 가열조건에 따른 분진과 PVC분말의 반응과정을 조사 검토하였다. 급격한 가열조건에서는 PVC의 분해에 의해 생성하는 염화수소 가스의 반응율이 66%정도로 낮을 뿐만 아니라 Fe의 휘발율도 20% 정도에 달하였다. 승온속도를 2℃/min으로 낮추면 염화수소 가스의 반응율이 95.3%까지 상승하고 Fe의 휘발을 완전히 억제할 수 있음을 확인 하였다. 또한 이 경우 반응과정에서 생성하는 FeCl2가 600℃ 이상에서 franklinite와 반응하여 ZnCl2와 Fe3O4를 생성시킴을 확인하였다. PVC를 40%혼합하여 제조한 펠릿을 2℃/min의 승온속도로 800℃까지 가열하고 수세함으로써 분진내에 함유되어 있던 아연과 납 그리고 카드뮴을 각각 96.2%, 97.4%, 98.8%회수 하였다. 수세과정을 거친 잔사는 중금속 함량이 작고 Fe와 C의 함량이 각각 46.0%와 20.9%로 높아 제철 공정에 재투입이 가능한 상태가 되었다.

키워드

분진

재활용

PVC

가열

휘발

아연

회수