A study on the recovery of heavy metals from electroplating waste water has been investigated using saponified PC-88A. The results showed that in the case of AA-type electroplating waste water, the extraction efficiencies of iron and zinc were not nearly affected by the saponification degree and were appeared to be 90% and 100%, respectively. Also, the extraction efficiencies of copper and nickel were higher than 90%, when the saponification degree was higher than 6% for copper and higher than 9% for nickel. On the other hand, hexavalent chromium ion as chromate(CrO42-) in the Cr-type electroplating waste water caused the decomposition of organic acid resulting from oxidating organic acid such as decanol and PC-88A. And, in the solvent extraction of CN-type electroplating waste water, iron, zinc, copper and nickel were extracted above 95% at the saponification degree of 6% with PC-88A of 25% and decanol of lower than 5%.
도금폐수로부터 중금속의 회수를 위한 용매추출 시 PC-88A의 비누화반응에 따른 추출특성을 조사하였다. 실험결과 AA계 도금폐수의 경우 철과 아연은 비누화도의 증가에 관계없이 추출률이 각각 90% 및 100% 정도로 거의 일정하게 나타나고 있으나, 구리는 비누화도 6% 이상에서 그리고 니켈은 비누화도 9% 이상에서 추출률이 90% 이상 나타나고 있다. 한편, Cr계 도금폐수의 경우 크롬산(CrO42-) 형태의 6가 크롬은 decanol이나 PC-88A등을 산화시켜 유기산의 분해를 초래한다. 그리고 CN계 도금폐수를 용매추출 할 경우 PC-88A의 농도 25%, decanol은 5% 이하로 하고 비누화도를 6% 정도로 하여 추출하면 철, 아연, 구리 및 니켈을 95% 이상 회수할 수 있다.
Click the PDF button.
- Publisher :The Korean Society of Mineral and Energy Resources Engineers
- Publisher(Ko) :한국자원공학회
- Journal Title :Journal of the Korean Society for Geosystem Engineering
- Journal Title(Ko) :한국지구시스템공학회지
- Volume : 40
- No :1
- Pages :33-39
Journal of the Korean Society of Mineral and Energy Resources Engineers