A study on the adsorption of hexavalent chromium and cyanide from electroplating waste water has been investigated using anion-exchange resins such as SA10AP, PA308, IRA 400 and IRA 904. The results showed that the adsorption efficiency of hexvalent chromium increased in proportion to amount of resin and SA10AP resin was more effective adsorbent for the adsorption of hexavalent chromium from Cr-type electroplating waste water. The desorption efficiency of hexavalent chromium from resin increased with increasing the weight ratio of NaCl / NaOH. On the other hand, PA308 resin was more effective adsorbent for the adsorption of cyanide from CN-type electroplating waste water and the cyanide was adsorbed more than 98% with resin of 20 g / l . Also, the adsorption efficiency of zinc and copper which formed complex ion with cyanide appeared to be higher considerably. The desorption of cyanide from resin was not nearly affected by the concentration of NaOH, but the desorption efficiency of cyanide appeared to be very low in the degree of 40%.
도금폐수로부터 Cr6+과 CN을 분리하기 위한 흡착시 음이온 교환수지의 종류와 첨가량에 따른 흡착특성에 대해 조사하였다. 실험결과 Cr계 도금폐수 중 Cr6+의 흡착률은 수지첨가량이 증가함에 따라 증가하고 있으며, SA10AP 수지가 Cr6+의 흡착에 가장 효과적인 것으로 나타났다. 그리고 Cr6+의 탈착시 NaCl/NaOH의 중량비가 증가할수록 탈착률이 급격히 증가하여 중량비 7에서 90% 정도가 탈착되었다. 한편, 시안(CN)계 도금폐수 중 CN의 흡착에는 PA308 수지가 효과적이고 수지첨가량 20 g / l에서 98% 이상 흡착되었으며, 시안과 착화합물을 형성하는 Zn와 Cu도 흡착률이 상당히 높게 나타나고 있다. 그리고 수지에 흡착된 CN의 탈착시 NaOH 농도의 영향은 거의 없는 것으로 나타났으며, 이와 함께 수지 단위 질량당 탈착액의 양을 증가시킴에 따라 CN의 탈착률이 약간씩 증가하나 20 ml / g-resin의 탈착액을 사용하여도 탈착률이 40% 수준으로 매우 낮게 나타났다.
Click the PDF button.
- Publisher :The Korean Society of Mineral and Energy Resources Engineers
- Publisher(Ko) :한국자원공학회
- Journal Title :Journal of the Korean institute of mineral and energy resources engineers
- Journal Title(Ko) :한국자원공학회지
- Volume : 39
- No :6
- Pages :462-469
Journal of the Korean Society of Mineral and Energy Resources Engineers