Saponite was synthesized with natural talc using a hydrothermal method. Synthesized saponite was characterized with XRD, SEM, DTA, TGA and infrared spectroscopy. XRD data showed that saponite was initially obtained at 190℃ and its crystallinity gradually increased as increasing heating temperature until 230℃. The results of TGA showed that greater weight reduction occurred at 230℃ than at 190℃. The DTA data for the range from room temperature to 150℃ showed clearly separated endothermal peaks at 102℃ and 137℃ for the synthesized sample at 230℃. This suggests that the synthesized saponite at 230℃ had a good crystallinity. Infrared spectra for the material formed above 230℃ also showed the typical patterns of saponite. The d-spacing of d001 did not change by heating until 700℃. It indicated that synthesized saponite did not change to heated-smectite. The SEM micrographs for saponite synthesized at various temperature showed that saponite crystal formed by a nucleation and epitaxial growth.
자연산 활석으로부터 수열법에 의해 사포나이트를 합성하였다. 합성된 사포나이트는 XRD, SEM, DTA, TGA 및 적외선 분광분석법에 의해 평가되었다. XRD 분석결과, 190℃에서 처음으로 사포나이트 결정이 확인되었으며, 230℃에서 우수한 결정도를 갖는 사포나이트가 합성되었음을 확인하였다. TGA 분석결과에서 230℃에서 190℃ 보다 더 많은 중량감소를 보였다. 상온에서 150℃의 온도범위에서의 DTA 분석결과에서 230℃ 시료에서 102℃ 및 137℃ 흡열피크의 확실한 분리를 확인할 수 있었으며 이를 통해 230℃에서 결정도가 우수함을 확인할 수 있었다. 또한, 적외선 분광분석에서도 230℃ 이상에서 전형적인 사포나이트 스펙트라를 볼 수 있었다. 합성한 사포나이트에 대해 열처리를 수행한 결과, 700℃까지 X-선 회절피크의 저면간격(d001)이 이동되지 않음은 사포나이트가 무수 스멕타이트로 변하지 않는다는 사실을 확인하는 것이다. 또한, 활석으로부터 수열법에 의해 합성한 사포나이트의 반응기구는, 반응온도에 따라 관찰된 SEM 상으로부터, 핵생성 및 에피탁셜 성장이라고 해석된다.
Click the PDF button.
- Publisher :The Korean Society of Mineral and Energy Resources Engineers
- Publisher(Ko) :한국자원공학회
- Journal Title :Journal of the Korean Society for Geosystem Engineering
- Journal Title(Ko) :한국지구시스템공학회지
- Volume : 41
- No :5
- Pages :347-353
Journal of the Korean Society of Mineral and Energy Resources Engineers